Triboelectric Nanogenerators Based on Nanostructured Layers of Zinc Oxide Deposited on Carbon Fabric

In this work, to obtain textile triboelectric layers for wearable flexible triboelectric nanogenerators (TENGs), we used two modes of growing nanostructured zinc oxide (ZnO) arrays on a carbon fabric (CF) using the automatic Successive Ionic Layer Adsorption and Reaction (SILAR) method. To produce a CF/ZnO_nr triboelectric textile with an array of intergrown short ZnO nanorods, we used a pre-coating of carbon fibers with ZnO seed layers. When the ZnO layer was fabricated by automatic SILAR on bare carbon fabric, we obtained the CF/ZnO_ns textile with an array of interconnected ZnO nanosheets 50–100 nm thick. As a proof of concept, we developed and tested two prototypes of flexible vertical contact–separation mode CF/ZnO_nr/PET/ITO and CF/ZnO_ns/PET/ITO TENGs, in which a gap was involuntarily formed between the smooth PET layer and the woven carbon textile coated with nanostructured ZnO films. In pressing tests with a force of ~5 N (pressure ~33 kPa), the CF/ZnO_ns/PET/ITO TENG created a higher open-circuit voltage up to 30 V and a higher maximum surface charge density of 1.3 μC/m2. In the successive press–release tests, this TENG showed an output voltage of 3.6 V, a current density of 1.47 μA/cm2, and a power density of 1.8 µW/cm2, confirming its effectiveness.