Abstract High Density Poly(ethylene) (HDPE) and Poly(propylene) (PP) were subjected to several surface treatments, namely UV grafting of hydroxyethylmethacrylate (HEMA), plasma deposition of HEMA and oxygen plasma treatment. Treated surfaces were subjected to two post-treatment routines (extraction with ethanol and high temperature aging). The effect of these treatments on the adhesion of HDPE and PP to epoxy coated studs was evaluated by a pull test. No adhesion at all was recorded on untreated samples. On the other hand, all the treatments yield high bond strength in the case of HDPE: an average bond strength of about 290 kg/cm2 and of about 200 kg/cm2 was observed after UV grafting and plasma treatments. The treated samples were practically insensitive to post-treatments. As to PP, which undergoes chain scission in plasma, it is best treated by the comparatively milder conditions of UV grafting, which yields an average bond strength similar to that observed on HDPE. O2 and HEMA-plasma-treated PP show a...
科研通智能强力驱动
Strongly Powered by AbleSci AI