Influence of the sintering temperature on the microstructure, mechanical properties and densification characteristics of (TiB + TiC)/TC4 composite

Abstract A hybrid of TiB whiskers and TiC particles reinforced TC4 matrix composites were in situ synthesized by spark plasma sintering (SPS) using a TC4-0.6wt.% B 4 C powder mixture at temperatures range from 550 °C to 1150 °C. The effect of sintering temperature on microstructure, grain size, mechanical properties and densification process of the (TiB + TiC)/ TC4 matrix composites were investigated. The composite sintered at 1050 °C has the highest tensile strength (1129.0 MPa), yield strength (1077.8 MPa) and plasticity (7.1%). The aspect ratio of TiB whiskers increases almost linearly below 1050 °C and its highest value is 33.2. The grain size of TiC increases with the increase of sintering temperature, and rapid growth occurs in the range of 850 °C to 950 °C. The composite sintered body appears four shrinkage stages before applying sintering pressure. The corresponding peak temperatures are 663 °C, 758 °C, 840 °C and 994 °C, respectively.