Correlation between weld formation and processing parameters in CO2 laser welding of steels

Laser welding, which has undergone rapid development in the past few decades, is one of the most important applications in laser materials processing. Although some general data are available, precise welding parameters are equipment specific. In the present study, a series of autogenous laser welds on mild and stainless steels has been investigated, using a Trumpf 3·0 kW CO2 laser system, to establish welding parameter windows. The correlation between laser power, welding speed, and weld bead profile for bead on plate welding has been obtained. For a constant laser power, penetration depth reaches a stable value as welding speed exceeds 11 000–13 000 mm min-1. This value is defined as the penetration threshold. Lower welding speed produces deeper penetration. However, under such conditions, the unstable keyhole and weld pool could result in undercut and porosity. The maximum penetration achievable for sound welds on both mild steel and stainless steel was investigated. The correlation between penetration threshold and power level was also established. The parameter windows established for autogenous welds can be adopted effectively on butt jointsif welding speed is reduced by 25%.