Optical Properties of Newly Developed Monolithic CAD/CAM Materials After Aging

Objective: With the widespread use of CAD/CAM (computer aided design and manufacture) systems in dentistry, many restorative materials have been produced. In our study, we aimed to evaluate the change in optical properties of newly developed translucent monolithic zirconia (TMZ) (Cercon HT Dentsply, Sirona, USA), zirconia-reinforced lithium silicate (ZLS) (Celtra Duo, Dentsply, Germany) and lithium disilicate (LS2) (IPS e.max CAD, Ivoclar Vivadent, Liechtenstein) materials with aging. Methods:10 discs of 12mm diameter and 1.2 mm thickness were produced from high translucent A2 color of each material. The aging process was applied in an autoclave under 134ºC, 0.2MPa pressure. For optical evaluation, L*, a*, b* values of the samples were measured by spectrophotometry before aging, after 3 hours and 6 hours aging. ΔE00 values and translucency parameters (TP) were calculated. The data were evaluated statistically. Results: In the present study, all the materials had undergone color change as a result of aging, but this change was within acceptable limits (ΔE00 0.8). There was a decrease in the translucency of all materials used in the study, but this decrease was not statistically significant. Conclusion: In the light of the findings obtained from this in vitro study, aging did not cause color and translucency changes in TMZ, ZLS, LS2 monolithic CAD/CAM materials.