Effect of annealing temperature on diamond/Si interfacial structure

Transmission electron microscope (TEM) observation showed that a 25 nm thick intermediate layer was formed at the diamond/Si bonding interface without annealing, the intermediate layer thickness decreased with the annealing temperature. No cracking even in nanometer scale occurred even after high-temperature annealing at 800 °C.