Sulfuric Acid Leaching of Zinc and Manganese from Spent Zinc-Carbon Battery

Characteristics on the sulfuric acid leaching of zinc and manganese from the spent zinc-carbon battery powders obtained by cushing and magnetic separation, were investigated with the variation of sulfuric acid concentration, reaction temperature, stir-ring speed and solid/liquid ratio. The sample powders were composed of Zn metal, ZnO, and . and it was found that the selective leaching of zinc was difficult in this system. At the condition of S/L ratio 1:10, IM H, and 200 rpm, leaching rate of Zn and Mn are 92% and 35% respectively. The concentration of Zn and Mn in the leaching solution are 19.5 g/l, 7.8 g/l and pH of that solution is 0.75. It was confirmed at reducing agent should be added to increase e leaching rate of manganese with sulfuric acid.