Influence of austenization temperature on microstructure and mechanical properties of a new ultra-high strength low alloyed steel

The effects of austenization temperature on the microstructures and mechanical properties of a newly designed ultra-high strength low alloy martensitic steel were systematically studied. The microstructures of the martensitic steels which were quenched from different temperatures between 860 and 980 °C were investigated by transmission electron microscopy (TEM) and electron backscatter diffraction (EBSD) and discussed. The results showed that the martensite laths were found to coarsen slowly and the carbide precipitates dissolved gradually with increasing austenization temperature. As the austenization temperature increased from 860 to 980 °C, the volume of retained austenite and the numerical ratio of high angle grain boundaries (HAGBs) were observed to increase while the numerical ratio of low angle grain boundaries (LAGBs) decreased. Rockwell C hardness (HRC), tensile strength and yield strength increased at first and then decreased, while impact toughness was greatly improved with increasing austenization temperature. The fracture mechanism was brittle fracture when austenitized at low temperatures, while it was ductile fracture when austenitized at high temperatures. The mechanical properties were significantly influenced by the formation of retained austenite, the dissolution of carbides, and the numerical ratio of HAGBs and LAGBs.