The Influence of Heat Treatment Temperature on Microstructure and Corrosion Behavior of SDSS Tube

The aim of this paper is to determine the proper heat treatment temperature for SDSS tube production without ${\sigma}$-phase precipitation. When Mother steel tube was heat treated at $800^{\circ}C$ temperature, relatively a large amount of ${\sigma}$-phase precipitated and grain refinement of ferrite phase occurred simultaneously. However, in Pilgered and Drawn steel tubes, grain refinement of the ferrite phase did not occur and a small amount of ${\sigma}$-phase precipitated. For all three types of steel tubes, the pitting potential was reduced to 2/5 or less compared with the untreated one and corrosion also occurred in the salt spray test due to the precipitation of ${\sigma}$-phase. When heat treatment temperature was $900^{\circ}C$, grain refinement of the ferrite phase occurred and very little ${\sigma}$-phase precipitated in Pilgered and Drawn steel tubes. But when heat treatment was done at $1,000^{\circ}C$ temperature, all three types of steel tubes had a similar corrosion properties of that of untreated one and also corrosion did not occur in the salt spray test, as ${\sigma}$-phase did not precipitate. Therefore, the optimum heat treatment temperature range is determined to be more than $1000^{\circ}C$ for the SDSS at which corrosion does not occur.