Evaluation of 3D Printing Orientation on Volume Parameters and Mechanical Properties of As-Build TI64ELI

The discovery of the utility of various titanium alloys as implant biomaterials has resulted in these materials becoming far more popular than other metals in the medical world. However, the production of these materials using additive manufacturing has its own challenges some of those being the surface finish that can be used as an implantology material. As such, the purpose of this study is to evaluate the influence of 3D-printed Ti64ELI on the as-built samples printed at 60°, 90°, and 180° orientations. Such studies are very limited, specifically in the development of the laser shock peening surface modification of dental implants. The study showed that each mechanical test that was performed contributes differently to the printing orientation, e.g., some tests yielded better properties when 180° printing orientation was used, and others had poorer properties when a 180° printing orientation was used. It was observed that 60° testing yielded a micro-hardness value of 349.6, and this value was increased by 0.37% when 90° orientation was measured. The lowest HV value was observed under a 180° orientation with 342.2 HV. The core material volume (Vmc) was 0.05266 mm3/mm2 at a 60° orientation, which increased by 11.48% for the 90° orientation. Furthermore, it was observed that the surface roughness (Sa) at 60° orientation was 43.68 μm. This was further increased by 6% when using the 90° orientation.