The Biocompatibility of Multi-Source Stem Cells and Gelatin-Carboxymethyl Chitosan-Sodium Alginate Hybrid Biomaterials

Nowadays, biological tissue engineering is a growing field of research. Biocompatibility is a key indicator for measuring tissue engineering biomaterials, which is of great significance for the replacement and repair of damaged tissues. In this study, using gelatin, carboxymethyl chitosan, and sodium alginate, a tissue engineering material scaffold that can carry cells was successfully prepared. The material was characterized by Fourier transforms infrared spectroscopy. In addition, the prepared scaffolds have physicochemical properties, such as swelling ratio, biodegradability. we observed the biocompatibility of the hydrogel to different adult stem cells (BMSCs and ADSCs) in vivo and in vitro. Adult stem cells were planted on gelatin-carboxymethyl chitosan-sodium alginate (Gel/SA/CMCS) hydrogels for 7 days in vitro, and the survival of stem cells in vitro was observed by live/died staining. Gel/SA/CMCS hydrogels loaded with stem cells were subcutaneously transplanted into nude mice for 14 days of in vivo culture observation. The survival of adult stem cells was observed by staining for stem cell surface markers (CD29, CD90) and Ki67. The scaffolds had a microporous structure with an appropriate pore size (about 80 μm). Live/died staining showed that adult stem cells could stably survive in Gel/SA/CMCS hydrogels for at least 7 days. After 14 days of culture in nude mice, Ki67 staining showed that the stem cells supported by Gel/SA/CMCS hydrogel still had high proliferation activity. Gel/SA/CMCSs hydrogel has a stable interpenetrating porous structure, suitable swelling performance and degradation rate, can promote and support the survival of adult stem cells in vivo and in vitro, and has good biocompatibility. Therefore, Gel/SA/CMCS hydrogel is a strong candidate for biological tissue engineering materials.