Structural and Phase Analysis of the Ausferritic Ductile Cast Iron Matrix Obtained by Heat Treatment and in the Raw State

This paper presents a comparative analysis of ausferritic ductile cast iron matrix obtained through heat treatment and in its raw state. Ausferrite without heat treatment was achieved by modifying the chemical composition, while nodular graphite was produced using Inmold technology. The presence of compacted graphite in the as-cast ausferritic cast iron was attributed to elements that impede the crystallization of nodular graphite. This study demonstrates that an ausferritic matrix in ductile cast iron can be achieved by incorporating molybdenum in conjunction with nickel or copper. Thermal and derivative analysis (TDA) revealed a minor thermal effect during the transformation of austenite into bainitic ferrite in as-cast ausferritic cast iron. Furthermore, the transformation of austenite in cast iron containing nickel was observed to occur at a temperature of approximately 60 °C higher than in cast iron with copper. The structure of bainitic ferrite platelets in as-cast ausferritic ductile cast iron resembled that of Austempered Ductile Iron (ADI). It was revealed that the amount of austenite in as-cast ausferritic ductile cast iron is more than double that in ADI. The carbon content of austenite was estimated theoretically, revealing that alloying additives in the as-cast ausferritic ductile cast iron reduce the solubility of carbon in austenite, thereby significantly influencing the properties of the cast iron.