Enhancement of Activity and Sulfur Resistance of CeO2 Supported on TiO2–SiO2 for the Selective Catalytic Reduction of NO by NH3

A series of novel metal-oxide-supported CeO(2) catalysts were prepared via the wet impregnation method, and their NH(3)-SCR activities were investigated. The Ce/TiO(2)-SiO(2) catalyst with a Ti/Si mass ratio of 3/1 exhibited superior NH(3)-SCR activity and high N(2) selectivity in the temperature range of 250-450 °C. The characterization results revealed that the activity enhancement was correlated with the properties of the support material. Cerium was highly dispersed on the TiO(2)-SiO(2) binary metal oxide support, and the interaction of Ti and Si resulted in greater conversion of Ce(4+) to Ce(3+) on the surface of the catalyst compared to that on the single metal oxide supports. As a result of in the increased number of acid sites on Ce/TiO(2)-SiO(2) that resulted from the addition of SiO(2), the NH(3) adsorption capacity was significantly improved. All of these factors played significant roles in the high SCR activity. More importantly, Ce/TiO(2)-SiO(2) exhibited strong resistance to SO(2) and H(2)O poisoning. After the addition of SiO(2), the number of Lewis-acid sites was not decreased, but the number of Brønsted-acid sites on the TiO(2)-SiO(2) carrier was increased. The introduction of SiO(2) further weakened the alkalinity over the surface of the Ce/TiO(2)-SiO(2) catalyst, which resulted in sulfate not easily accumulating on the surface of the Ce/TiO(2)-SiO(2) catalyst in comparison with Ce/TiO(2).