Effects of Over-burnt Bricks on Gradation, Water Absorption and Specific Gravity of Aggregates, Workability and Compressive Strength of Concrete

Demand of bricks is increasing day by day by the requirement of new structures. Due to manufacturing of bricks, over-burnt bricks are also made. Generally over-burnt bricks are the waste materials which is generally used for dumping purpose and sometime it is thrown in useful land that create social and environmental problems. Therefore, this material should be properly treated, recycled and used in concrete as coarse aggregate. In this research work, six (06) batches were made with 1:2:4 mix and 0.5 water cement ratio. Each batch consists of five (05) samples. Six (06) batches were made with 0%, 20%, 40%, 60%, 80% and 100% replacement of natural coarse aggregates with over-burnt bricks aggregates. The outcome of study reveals that the gradation of both the aggregates shows same pattern and the trend of curve was almost similar, with minor difference in range values over a sieve. The water absorption of over-burnt bricks aggregates was more than the water absorption of natural coarse aggregates and the specific gravity of over-burnt bricks aggregates was less than the specific gravity of natural coarse aggregates. The result of slump test shows that there was continuous decrease in workability of concrete mix, as replacement of over-burnt bricks aggregates increased. 30 concrete cubes of (6” x 6” x 6”) size were prepared and cured for 28 days followed by compressive strength. The result shows that the concrete derived from over-burnt bricks aggregates attained lower compressive strength than the regular concrete. However, the values obtained from over-burnt bricks aggregates are still acceptable, especially for reasonable levels of the replacement ratio up-to 60%. This concrete can be used in new constructions, but it is proposed to be initially utilized in low load areas.