Corrosion Effects on Bond Degradation and Cracking Patterns in Lapped Spliced Joints of Reinforced Concrete

This research study aims to enhance the understanding of corrosion behaviour in lapped spliced joints within reinforced concrete structures. Specifically, the effect of corrosion on bond degradation and crack formation is investigated. Accelerated corrosion tests were conducted on two sets of semi-cylindrical samples and half-beam blocks. By applying a constant voltage, the current-time relationship during the corrosion process was obtained. Subsequently, the samples were subjected to pull-out testing to assess their bond strength. Three primary modes of bond failure were observed: pull-out, splitting, or a combination of both. Notably, the results demonstrate that the reduction in bond strength is directly related to the corrosion level, considering factors such as mass loss, section loss, and diameter reduction. Furthermore, a strong correlation exists between corrosion-induced cracks and the weakening of bond strength. These findings align with existing research and enrich the experimental data in the current corrosion database for lap splice joints in reinforced concrete structures.