Assembled hybrid films based on sepiolite, phytic acid, polyaspartic acid and Fe3+ for flame-retardant cotton fabric

Abstract To impart durable flame retardant property to cotton fabric, a kind of multilayered hybrid film based on environmentally friendly phytic acid, sepiolite, polyaspartic acid, and Fe 3+ were deposited on the surface of cotton fabric by layer-by-layer and spraying method to form a dense protective layer. Compared with cotton fabric, hybrid film coated cotton showed excellent flame retardant property and low fire hazard, which can be demonstrated by vertical flame test, limiting oxygen index (LOI) and cone calorimeter test. After-flame time and after-glow time of hybrid film coated cotton is 1 s and 1 s, respectively. LOI value of hybrid film coated cotton increased by 44.4% compared with control sample. Cone calorimeter test revealed a total heat release rate reduction of 52.6% and peak heat release rate reduction of 73.6% for hybrid film coated cotton fabric. This work demonstrates that the hybrid film composed of phytic acid, sepiolite, polyaspartic acid, and Fe 3+ could improve the durable flame retardant property of cotton fabric.