Spatially heterogeneous degradation in LiFePO4//graphite pouch batteries under temperature accelerated aging process

Temperature-accelerated aging behavior of LiFePO 4 //graphite batteries was investigated, highlighting spatial heterogeneity between inner and outer electrodes. The degradation disparity offers new insights into temperature-induced failure mechanisms.