Organosilane Modification of Lignin and Lignosulfonate: Structure and Compatibility in PVDF Membrane

The high difference in surface tension between the filler and the polymer often constrains membrane compatibility. To reduce the surface tension, organosilane such as GPTMS is usually used to improve miscibility. In this study, GPTMS was introduced to produce lignin-GPTMS (LG) and lignosulfonate-GPTMS (LsG). The modification was done by reacting lignin and lignosulfonate with GPTMS using ethanol as the media. The product was characterized using Fourier Transform InfraRed (FTIR), X-ray Diffraction (XRD), Particle Size Analyzer (PSA), Scanning Electron Microscope-Energy Dispersive X-ray (SEM-EDX) and microscope. The success of functionalization was shown in FTIR spectra with the vibration of Si-O at 1034 cm-1 and 528 cm-1. The XRD analysis presents that the filler material has an amorph and crystalline structure. The functionalization using a 2:1 ratio increases zeta potential absolute and particle size due to the silane being a bridge and making a larger macromolecule. For a ratio of 1:1, a higher organosilane compound results in breaking siloxane linkages and making smaller molecules. Mixed LG and LsG into PVDF membrane conducted to analyze filler compatibility. The sulfonation and functionalization of GPTMS increase the compatibility of lignin in PVDF membrane with the best homogeneity achieved by a membrane with the addition of LsG 1:1.