Preparation and Property Study of Organosilicon Antisticking Coatings

In this article, an organosilicon antisticking coating was synthesized from vinyl silicone oil, hydrogen-containing silicone oil, and platinum catalyst. Firstly, the methyl vinyl MQ (mono and quad) silicone resin was added. When the silicone content was 30 wt.%, the shore hardness and tensile strength increased to about 27.4% and 115.9%, respectively. Furthermore, nano-SiO 2 powder was added to further improve its antisticking property. This was due to the change of the surface roughness, which could greatly improve the antisticking performance. When the nano-SiO 2 powder content was 2 wt.%, the surface free energy and antisticking force were the lowest and the antisticking effect was the best as well and the mechanical properties of silicone rubber had been improved.