From water reduction to oxidation: Janus Co-Ni-P nanowires as high-efficiency and ultrastable electrocatalysts for over 3000 h water splitting

Vertically-aligned cobalt nickel phosphide nanowires (Co-Ni-P NWs) are synthesized on Ni foam by phosphorizing cobalt carbonate hydroxide precursor NWs in red phosphorous vapor at an elevated temperature. The as-fabricated self-supported integrated electrode ([email protected]) exhibits outstanding electrocatalytic activity for the hydrogen evolution reaction (HER) in alkaline solution, delivering a cathodic current density of 100 mA cm−2 at a small overpotential of 137 mV and a Tafel slope of 65.1 mV dec−1. Furthermore, the electrode shows remarkable catalytic performance towards the oxygen evolution reaction (OER), affording an anodic current density of 90.2 mA cm−2 at an overpotential of 350 mV, superior to many other transition metal based OER catalysts. Given the well-defined bifunctionality, an alkaline electrolyzer is assembled using two symmetrical [email protected] as the cathode and anode, respectively, which demonstrates outstanding catalytic performance for sustained water splitting at varying current densities from 10 to 240 mA cm−2. Significantly, the [email protected] electrolyzer is able to operate for 3175 h (ca. 132 days) without degradation at an industry-relevant current density of 100 mA cm−2, leading to exceptionally high H2 production rate of 311 mmol h−1 g−1catalyst cm−2 with an energy efficiency of 76% at ca. 1.9 V.