Dual-wavelength and efficient continuous-wave operation of a Yb:CaGd0.1Y0.9AlO4laser

The spectra and laser properties of single crystalline Yb:CaGd0.1Y0.9AlO4 were investigated for the first time. The peak absorption cross-sections of 4.01 cm2 and 1.39 × 10−20 cm2 with full width at half maximum of 17 and 32 nm, and the maximum emission cross-sections of 2.11 and 1.53 × 10−20 cm2 were obtained for π and σ polarizations, respectively. The fluorescence decay time was 638 µs. The maximum continuous-wave laser achieved was 1.60 W with a slope efficiency of 23.4% for an a-cut Yb:CaGd0.1Y0.9AlO4 crystal. Dual-wavelength lasers at 1041.7 and 1044.9 nm were also demonstrated. The results show that Yb:CaGd0.1Y0.9AlO4 crystal is a promising ultra-short and dual-wavelength laser medium.