Effect of Thermal Annealing for MgGa2Se4Single Crystal Thin Film Grown by Hot Wall Epitaxy

The evaporating materials for $MgGa_2Se_4$ single crystal thin films was prepared from horizontal electric furnace. To obtain the single crystal thin films, $MgGa_2Se_4$ compounded polycrystal powder was deposited on thoroughly etched semi-insulated GaAs(100) substrate by the hot wall epitaxy (HWE) method system. The source and substrate temperatures of optimized growth conditions, were $610^{\circ}C$ and $400^{\circ}C$, respectively.The source and substrate temperatures were $610^{\circ}C$ and $400^{\circ}C$, respectively. The crystalline structure of the single crystal thin films was investigated by double crystal X-ray diffraction (DCXD). The temperature dependence of the energy band gap of the $MgGa_2Se_4$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)=2.34\;eV-(8.81{\times}10^{-4}\;eV/K)T^2/(T+251\;K)$. After the as-grown $MgGa_2Se_4$ single crystal thin films was annealed in Mg-, Se-, and Ga-atmospheres, the origin of point defects of $MgGa_2Se_4$ single crystal thin films has been investigated by the photoluminescence (PL) at 10 K. The native defects of $V_{Mg}$, $V_{Se}$ obtained by PL measurements were classified as a donors or acceptors type. And we concluded that the heat-treatment in the Se-atmosphere converted $MgGa_2Se_4$ single crystal thin films to an optical n-type. Also, we confirmed that Ga in $MgGa_2Se_4$/GaAs did not form the native defects because Ga in $MgGa_2Se_4$ single crystal thin films existed in the form of stable bonds.