Corrigendum: Highly Reversible Zinc Anode Achieved by Surface Polyimide Coating for High‐Performance Aqueous Zinc‐Ion Batteries

The contact angle was incorrectly marked in Figure 2g,h)."Compared with bare zinc (91.46°), the PI-Zn owns a smaller contact angle (76.69°) in 3 M Zn(CF 3 SO 3 ) 2 electrolyte (Figure 2g-h)".is corrected to "Compared with bare zinc (80.8°), the PI-Zn owns a smaller contact angle (65.7°) in 3 M Zn(CF 3 SO 3 ) 2 electrolyte (Figure 2g-h)".The correct Figure 2 is shown below.The information reported in the abstract, introduction, results, and conclusions are valid.The authors sincerely apologize for any inconvenience caused by this correction.Figure 2. SEM images of the top-surfaces of bare Zn in a) pristine state, b) 50 cycles, c) 100 cycles; SEM images of the top-surfaces of PI-Zn in d) pristine state, e) 50 cycles, f ) 100 cycles; Contact angles of g) bare Zn and h) PI-Zn foils in the electrolyte; i) XRD pattern of bare Zn and PI-Zn foils after 50 charge/ discharge cycles at 1 mA cm À2 .