A new gelcasting using Isobam both as dispersant and monomer

Gelcasting is a kind of colloidal processing with many attractive advantages for fabricating ceramics. In this study, a new and simple gelcasting system with only two additives was investigated using Isobam (a copolymer of isobutylene and maleic anhydride) both as dispersant and monomer, and Tetraethylenepentamine (TEPA) as crosslinker. The gelation studies in solutions showed the reaction between Isobam and TEPA was an acylation reaction which was controlled by temperature and concentration. The rheological behavior and samples' properties of 50 vol% Al2O3 slurries with different Isobam contents were studied. With 8 wt% of Isobam by water, the dried green bodies had relatively density of 56.3% and flexural strength of 25.7 ± 2.2 MPa. After sintering at 1530 °C for 3 h, the relatively density and flexural strength of sintered ceramics were 98.7% and 416 ± 19 MPa respectively. The SEM and macroscopic results showed that dried green bodies and sintered ceramics with homogeneous and defect–free morphology were obtained by using Isobam–TEPA system.