Effect of Heat Treatment on Microstructure and Mechanical Properties of High-Strength Steel for in Hot Forging Products

High-strength steel is widely used in hot forging products for application to the oil and gas industry because it has good mechanical properties under severe environment. In order to apply to the extreme environment industry requiring high temperature and high pressure, heat treatments such as austenitizing, quenching and tempering are required. The microstructure of high-strength steel after heat treatment has various microstructures such as Granular Bainite (GB), Acicular Ferrite (AF), Bainitic Ferrite (BF), and Martensite (M) depending on the heat treatment conditions and cooling rate. Especially in large forged products, the difference in microstructure occurs due to the difference in the forging ratio depending on the location and the temperature gradient according to the thickness during post-heat treatment. Therefore, this study attempted to quantitatively analyze various phases of F70 high-strength steel according to the austenitizing temperature and hot forging ratio using the existing EBSD analysis method. In addition, the correlation between microstructure and mechanical properties was investigated through various phase analysis and fracture behavior of high-strength steel. We found that various microstructures of strength steel depend on the austenitizing temperature and hot forging ratio, and influence the mechanical properties and fracture behavior.