Huazhang Zhao,Yanji Zhang,Wenxia Li,Ruiying Liang,Xiangcheng Mi,Haijie Sun,Xiuling Liu,Yanping Wang
标识
DOI:10.1016/j.optmat.2024.115148
摘要
LiAl4O6F (LAOF): Mn4+, Na+, Ga3+ red fluorescent materials were prepared by high temperature solid phase method. The properties of LAOF: Mn4+, Na+, Ga3+ phosphors were characterized by X-ray diffraction (XRD), photoluminescence (PL) spectra, variable temperature spectroscopy, scanning electron microscopy (SEM) and other tests. Under the excitation of 450 nm light, an intense red emission peak was observed around 662 nm, corresponding to the 2Eg→4A2g transition of Mn4+. Compared with Mn4+ single doping, the introduction of Na+, Ga3+ greatly improves the luminescence intensity of LAOF. The photoluminescence quantum yield of the optimal LAOF: 0.2%Mn4+, 0.2%Na+, 3%Ga3+ phosphor was measured to be 41.6%. The prepared sample have excellent thermal and water stability. Meanwhile, the w-LED device with a beneficial luminescence efficiency (LE = 331.7 lm W−1), exhibited good CRI and CCT values. These results indicate that LAOF: Mn4+, Na+, Ga3+ phosphors have potential application prospects as a red component in the field of lighting display.
科研通智能强力驱动
Strongly Powered by AbleSci AI