Fabrication of Tungsten Powder Mixtures with Nano and Micro Size by Reduction of Tungsten Oxides

An optimum route to fabricate a hybrid-structured W powder composed of nano and micro size powders was investigated. The mixture of nano and micro W powders was prepared by a ball milling and hydrogen reduction process for WO3 and W powders. Microstructural observation for the ball-milled powder mixtures revealed that the nano-sized WO3 particles were homogeneously distributed on the surface of large W powders. The reduction behavior of WO3 powder was analyzed by a temperature programmed reduction method with different heating rates in Ar-10% H2 atmosphere. The activation energies for the reduction of WO3, estimated by the slope of the Kissinger plot from the amount of reaction peak shift with heating rates, were measured as 117.4 kJ/mol and 94.6 kJ/mol depending on reduction steps from WO3 to WO2 and from WO2 to W, respectively. SEM and XRD analysis for the hydrogen-reduced powder mixture showed that the nano-sized W particles were well distributed on the surface of the micro-sized W powders.