Synthesis and Effect of Ammonium 2,2′-Methylene-bis-(4,6-di-t-Butylphenylene) Phosphate as Nucleating Agent of Poly(Propylene)

A nonmetallic organophosphate salt, ammonium 2,2′- methylene-bis-(4,6-di-t-butylphenylene) phosphates (An), was synthesized via a simple method, and its application in iPP as a nucleating agent was investigated. Differential scanning calorimetry (DSC) result showed the melting temperature of An was 262°C, and SEM (scanning electron microscopy) observations indicated that its crystallization morphology was lamellar shape with a quite smooth surface. The crystallization behavior of nucleated isotactic poly(propylene) (iPP) containing An demonstrated that An can effectively raise the crystallization peak temperature and reduce the spherulite size, resulting in obviously improved strength and transparency. The tensile and flexural strength of iPP nucleated with An was increased by 11% and 32%, respectively. The haze value of iPP/An was decreased from 36.7% to 15.5%. These results revealed that this organophosphate ammonium salt can be used as an effective nucleating agent of iPP and provides a new organophosphate salt type nucleating agent for polymers.