Synthesis and characterization of polyaniline-based composites using cellulose nanocrystals as biological templates

Polyaniline (PANI) is considered as an ideal electrode material due to its remarkable Faradaic activity, exceptional conductivity, and ease of processing. However, the agglomeration and poor cycling stability of PANI largely limit its practical utilization in energy storage devices. To address these challenges, PANI was synthesized via a facile one-pot, two-step process using cellulose nanocrystals (CNCs) as bio-templates in this work. Zeta potential and particle size measurements revealed that the CNC template could impart improved dispersion stability to the synthesized PANI, which exhibited a decrease in average particle size from 1100 nm to 300 nm as a function of 10 % CNCs. Furthermore, the effect of CNC loadings on the performance of PANI was systematically investigated. The results showed that the specific capacitance of PANI/CNC increased from 102.52 F·g−1 to 138.12 F·g−1 with the CNC loading increase from 0 to 10 wt%. Particularly, the PANI/CNC composite film with a 1:9 ratio (C-P-10 %) demonstrated a capacity retention of 84.45 % after 6000 cycles and an outstanding conductivity of 526 S·m−1. This work generally offers an effective solution for the preparation of high-performance PANI-based composites, which might hold great promise in energy storage device applications.