Introducing self-healing properties to polyethersulfone (PES) membrane via poly(vinyl alcohol)/ polyacrylic acid (PVA/PAA) surface coating

During membrane filtration , it is inevitable that a membrane will experience physical damage, leading to a loss of its integrity and a decrease in separation efficiency. Hence, the development of a water-responsive membrane capable of healing itself autonomously after physical damage is significantly important in the field of water filtration . Herein, a water-enabled self-healing composite polyethersulfone (PES) membrane was synthesized by coating the membrane surface using a mixed solution composed of poly (vinyl alcohol) and polyacrylic acid (PVA-PAA). The self-healing efficiency of the coated PES membrane was examined based on the changes in water flux at three stages which are pre-damaged, post-damaged, and post-healing. The self-healing process was initiated by the swelling of the water-responsive PVA and PAA, followed by the formation of reversible hydrogen bonds , completing the self-healing process. The coated PES membrane with three layers of PVA-PAA coatings (at 3:1 ratio) demonstrated high water flux and remarkable self-healing efficiency of up to 98.3%. The self-healing capability was evidenced by the morphology of the membrane observed via scanning electron microscope (SEM). The findings of this investigation present a novel architecture approach for fabricating self-healing membranes using PVA-PAA, in addition to other relevant parameters as reported. • PES membrane coated with PVA/PAA mixture exhibited self-healing properties. • Reversible hydrogen bonds allow the modified membrane to self-heal. • The damaged membrane showed recovery in flux and rejection. • More coating layers and longer healing time could improve the recovery of the damaged membrane.