Influence of the extreme grain size reduction on plastic deformation instability in an AlMg and AlMgScZr alloys

The elaboration of new alloys sustains a strong interest to the phenomenon of unstable plastic flow, or the Portevin–Le Chatelier (PLC) effect, caused by interaction of dislocations with solute atoms. Moreover, this effect attracts interest as a rich example of self-organization in dynamical systems. It is associated with complex patterns of stress serrations related to nucleation and motion of deformation bands in the deforming material, and requires understanding of self-organization of dislocations. Plastic deformation of Al-Mg alloys is prone to instability in a wide range of experimental conditions. For this reason, binary Al-Mg alloys served for a long time as model objects for investigation of the PLC effect. At the same time, the practical use of binary Al-Mg alloys is limited because of their low strength. A significant improvement of their properties can be achieved by additional alloying, in particular, leading to precipitation. Further, extensive grain refinement could be a key technique used to produce tough and high- strength materials. However, there exists very limited and often contradictory information on the PLC instability in fine-grained Al-Mg alloys containing precipitates. The objective of the present thesis was to investigate specific features of the PLC effect in AlMg-based alloys with and without nanoscale particles, both in coarse-grained and fine-grained states, the latter obtained by severe plastic deformation. Using local extensometry methods, particularly the image correlation technique, these studies revealed an unusual persistence of the propagation of deformation bands in alloys with precipitates and/or fine grains. This dynamic mode is observed in a wide range of strain rates, whereas it only appears at high strain rate in model Al-Mg alloys. Moreover, the analysis of statistical distributions of stress drop amplitudes revealed a tendency to power law statistics characteristic of the propagation mode. This phenomenon was attributed to a modification of the spatial coupling between dislocations due to the concentration of internal stresses. The combination of these studies with the acoustic emission analysis uncovered an influence of the microstructure on the competition between a random factor and the dislocation synchronization. Finally, the study by the image correlation made it possible to observe an interrelation between the PLC instability and the neck formation.