Effect of Nb-Mo additions on precipitation behaviour in V microalloyed TRIP-assisted steels

The microstructural evolution and precipitation behaviour of Nb-V-Mo and single V containing transformation-induced plasticity-assisted steels with an acicular/bainitic ferrite matrix were investigated by a heat treatment up to the austenite formation range. It was found that during the heating stage the acicular/bainitic ferrite matrix resisted recrystallisation, while cementite and martensite were decomposed and austenite was formed in the acicular/bainitic ferrite. Both Nb-V-Mo and V containing steels after the heat treatment showed a microstructure consisting of a polygonal ferrite matrix with small islands of pearlite. During these transformations, the microscopy observations showed that 0.04 wt% Nb and 0.08 wt% Mo additions to the 0.16 wt% V microalloyed steel considerably reduced the growth-coarsening of microalloy precipitates.