Removal of Low-Content Impurities from Pure Al by Supergravity Combined with Semi-Solid Method

Recently, the purification technology for high-purity aluminum (Al) has become the focus and difficulty of the majority of researchers. In this study, a novel approach for removing iron (Fe) impurities from pure Al via combining the supergravity field and semi-solid refining was proposed. Various separation temperatures (T), holding times (th), and separation times (ts) were applied within a gravitational field to explore their impact on the purification process and its underlying mechanisms. The optimal conditions were achieved at T = 653 °C, th = 40 min, ts = 3 min, and a gravity coefficient G = 1000, with the loss rate of purified Al reaching up to 4.1% and the removal rate of Fe reaching 81.9%. The Fe content in pure Al was reduced from 0.32 wt.% to 0.06 wt.%. Moreover, the purified mechanism of supergravity in a semi-solid method was reported for the first time. It was concluded that supergravity could decrease the value of the effective distribution coefficient (ke), thereby promoting the continuous migration of Fe impurities at the solidification interface into the liquid phase. The Fe-rich phase in the Al melt was completely filtered to the lower part of the crucible in the supergravity field, completing the further purification of the pure Al.