Upgrading poly(butylene succinate)/wood fiber composites by esterified lignin

Aliphatic chains were introduced into the macromolecule of kraft lignin using aliphatic chlorides as esterification reagents. The hydrophobicity of esterified lignin (EL) was enhanced as compared to the original lignin. EL was further used as a macromolecular coupling agent in poly(butylene succinate)/chemi-thermomechanical pulp fiber composites. As a result, the composites with enhanced mechanical performance were obtained, and the tensile strength, impact strength, and bending strength were increased by 25.1, 22.4, and 19.3%, respectively, under 2 wt% EL-treatment (synthesized by palmitoyl chloride, –COCl/–OH = 1.5:1) in comparison with those of the specimen without any coupling agent treatment. Furthermore, the composite prepared with EL-treated fibers shows significant lower water absorption ratio than that of untreated one. A significant increase in storage modulus (E′) was observed upon the incorporation of treated fibers. Furthermore, the improved interfacial bonding between treated fibers and matrix was verified by SEM images. The shear viscosity of composite was increased by the incorporation of EL, but in general, the rheological behaviors of composites are not significantly changed.