Heat Treatment of AZ91-5wt.%Sn Magnesium Alloy

The microstructure, electrical conductivity and hardness variation of an AZ91-5wt%Sn Mg alloy sample during a solid-solution and aging heat treatment were instigated by optical microscopy, scanning electron microscopy, X-ray diffraction and by Rockwell hardness techniques in this study. The XRD result shows that the main phases in the as-casted alloy are ${\alpha}$-Mg, $Mg_{17}Al_{12}$ and $Mg_2Sn$. From the SEM images of the AZ91-5wt%Sn Mg alloy after the solution treatment, the $Mg_{17}Al_{12}$ phases in the alloy were found to have dissolved into the matrix with an increase in the holding time during the solution treatment, but $Mg_2Sn$ phases were clearly observable. The highest peak hardness of the AZ91-5wt%Sn Mg alloy is 82HRE at an aging temperature of $200^{\circ}C$.