A Study of Modification of M2 Cast High Speed Steel

Abstract M2 cast high speed steel was inoculated by addition of rare earth(RE)‐Al‐N, network eutectic carbides were eliminated, matrix structures were refined and the segregation of tungsten and molybdenum elements were relieved. In the condition that the hardness did not decrease, impact toughness obviously increased. Quenching at 1180 °C and three‐times tempering at 560 °C, the hardness of M2 cast high speed steel kept 65~66HRC, impact toughness reached 21.3J/cm 2 . Modified M2 cast high speed steel had excellent thermal fatigue resistance and high temperature wear resistance. Roll made in modified M2 cast high speed steel had excellent service effect using in slit rolling mill stand of hot rolling bar mill.