Water Absorption Behavior of Polystyrene Particles Prepared by Emulsion Polymerization with Nonionic Emulsifiers and Innovative Easy Synthesis of Hollow Particles

Submicrometer-sized raspberry-like polystyrene (PS) particles, which were prepared by emulsion polymerization with polyoxyethylene nonylphenyl ether nonionic emulsifier (Emulgen 910, HLB 12.2) and potassium persulfate initiator, contained 8.5 vol % (relative to the particle) of water and 5.5 wt % (relative to PS) of Emulgen 910 in the inside. The water absorption decreased the glass transition temperature of the PS particles dispersed in an aqueous medium. The wt % (relative to PS) of the incorporated Emulgen 910 increased with increasing initial Emulgen 910 concentration in the emulsion polymerization, but the wt % (relative to the total Emulgen 910 used) of the incorporated Emulgen 910 was constant at approximately 50% independent of the initial concentration. The vol % (relative to particle) of water increased to 46% by heat treatment at 90 °C for 24 h, which was based on further water absorption, and resulted in spherical hollow particles, where the amount of the incorporated Emulgen 910 remarkably de...