Properties of hafnium oxide films grown by atomic layer deposition from hafnium tetraiodide and oxygen

Polycrystalline monoclinic HfO2 films were atomic layer deposited on Si(100) substrates by a nonhydrous carbon-free process of HfI4 and O2. The oxygen to hafnium ratio corresponded to the stoichiometric dioxide within the limits of accuracy of ion beam analysis. A 1.5–2.0 nm thick SiO2 interface layer formed between the HfO2 films and Si substrates. Hysteresis of the capacitance–voltage curves was observed in Al/HfO2/p-Si(100) structures with oxide grown in the substrate temperature range of 570–755 °C. The hysteresis ceased with an increase in O2 pressure. The effective permittivity of the dielectric layers varied between 12 and 16. The breakdown voltages were found to be lower in the case of higher oxygen doses and higher HfO2 deposition temperatures.