Influence of Melt Infiltration Parameters on Structural and Mechanical Properties of Al-4.3wt.%Cu-EP Syntactic Foam

The present research concerns fabrication of Al-4.3wt.%Cu metal syntactic foams using expanded perlite particles (EPPs). A gas pressure infiltration technique was employed to fabricate the aluminium syntactic foams under different infiltration temperatures and pressures. Ambient air pressure and 750 °C were identified as the favoured processing conditions for full infiltration of the melt. The average density and EP volume percentage of the fabricated foams were measured to be about 1.55 g/cm3 and 50.3%, respectively. Melt infiltration is believed to be mainly controlled by the breakage of the aluminium oxide layer on the melt surface and melt viscosity. Preferential infiltration of the melt between the mould wall and the EP particles bed complemented by radial melt infiltration toward the centre of the samples was identified. The effects of EP particles on growth of the nucleated primary α-aluminium phase were discussed. XRD and EDS analyses suggested some chemical reactions at the interface of EPPs with the molten aluminium. T6 heat treatment in the ambient atmosphere improved the average compressive tensile strength, plateau stress, and absorption capacity of the syntactic foams by more than 100%. Uniform deformation and similar densification strains (about 40%) of the as-fabricated and heat-treated syntactic foams during the compression test suggested uniform distribution of EP particles and metallic struts in the aluminium alloy matrix.