摘要
This study examined the stability of rapid sulphoaluminate cement concrete (R-SACC) when exposed to heat for extended periods of time. The physicochemical processes present in R-SACC as a function of temperature were determined through various tests. The general behavior of rapid sulphoaluminate cement (R-SAC) at a range of temperatures is summarized. The results show that observing color change could be a simple way to identify deterioration of R-SACC, along with the rebound hammer. The matrix formation of ettringite was broken and the mass of the hydrated product decreased with heat exposure; the major mineral composition of the paste consisted of CaSO4, CaCO3 and β-C2S; and the interface between aggregate and paste in the R-SACC become loosely structured with cracks. Between 50°C and 120°C, the rapid sulphoaluminate cement (R-SAC) paste first expanded and then shrank, and the shrinkage rate of R-SAC was much greater than that of R-SACC.
科研通智能强力驱动
Strongly Powered by AbleSci AI