Ductility of 0.1-0.6C-1.5Si-1.5Mn Ultra High-strength TRIP-aided Sheet Steels with Bainitic Ferrite Matrix

The effects of heat treatment and forming conditions on retained austenite characteristics and ductility of 0.1-0.6C-1.5Si-1.5Mn, mass%, ultra high-strength TRIP-aided sheet steels with bainitic ferrite matrix were investigated. These steels possessed large total elongations of about 20-25% in a tensile strength ranging from 700 to 1300 MPa when austempered at temperatures above martensite-start temperature (MS). The total elongations were enhanced by warm forming at two temperatures, TP1 and TP2. The first peak forming temperatures TP1s were between 0°C and 75°C and were nearly constant regardless of carbon content of the steels. This was associated with the strain-induced martensite transformation of a large amount of metastable retained austenite which suppressed a rapid fall of strain-hardening rate in an early strain range to resultantly increase the uniform and total elongations. On the other hand, the second peak forming temperatures TP2s were between 200 and 300°C and further large total elongations beyond 30% were achieved in high carbon steels (0.4% C and 0.6% C steels) with tensile strength of 1300-1500 MPa. The large improvement was controlled by both the strain-induced bainite transformation and dynamic strain aging.