Effect of ferroelectric and interface films on the tunneling electroresistance of the Al2O3/Hf0.5Zr0.5O2 based ferroelectric tunnel junctions

Ferroelectric random-access memory (FRAM) based on conventional ferroelectric materials is a non-volatile memory with fast read/write operations, high endurance, and 10 years of data retention time. However, it suffers from destructive read-out operation and lack of CMOS compatibility. HfO2-based ferroelectric tunnel junctions (FTJ) may compensate for the shortcomings of FRAM by its CMOS compatibility, fast operation speed, and non-destructive readout operation. In this study, we investigate the effect of ferroelectric and interface film thickness on the tunneling electroresistance or ON/OFF current ratio of the Hf0.5Zr0.5O2/Al2O3based FTJ device. Integrating a thick ferroelectric layer (i.e. 12 nm Hf0.5Zr0.5O2) with a thin interface layer (i.e. 1 nm Al2O3) resulted in an ON/OFF current ratio of 78. Furthermore, to elucidate the relationship between ON/OFF current ratio and interfacial properties, the Hf0.5Zr0.5O2-Al2O3films and Ge-Al2O3interfaces are examined via time-of-flight secondary ion mass spectrometry depth profiling mode. A bilayer oxide heterostructure (Hf0.5Zr0.5O2/Al2O3) is deposited by atomic layer deposition (ALD) on the Ge substrate. The ON/OFF current ratio is enhanced by an order of magnitude when the Hf0.5Zr0.5O2film deposition mode is changed from exposure (H2O) ALD to sequential plasma (sequential O2-H2) ALD. Moreover, the interfacial engineering approach based on thein situALD H2-plasma surface pre-treatment of Ge increases the ON/OFF current ratio from 9 to 38 by reducing the interfacial trap density state at the Ge-Al2O3interface and producing Al2O3with fewer oxygen vacancies as compared to the wet etch (HF + H2O rinse) treatment of the Ge substrate. This study provides evidence of strong coupling between Hf0.5Zr0.5O2and Al2O3films in controlling the ON/OFF current ratio of the FTJ.