Azri Azmi,K. Y. Lau,Noor Azlinda Ahmad,Zulkurnain Abdul‐Malek,Chee Wei Tan,Kuan Yong Ching
标识
DOI:10.1109/pecon48942.2020.9314448
摘要
This paper reports on the effects of aging on thermal and dielectric properties of unfilled polypropylene and polypropylene nanocomposites containing 2 wt% and 5 wt% of magnesium aluminate nanofiller. These evaluated samples were prepared using a melt blending technique. A hydraulic laboratory press was employed in order to obtain 100 μm thick sample. Two different aging conditions were considered, namely, unaged (as a reference) and aged at 140 °C. The evaluated samples were then characterized using differential scanning calorimetry (DSC) for thermal analysis. Meanwhile, the dielectric strength was determined based on DC electrical breakdown tests. The experimental results show that, aging the samples at 140 °C changed the thermal behavior of all evaluated samples. Specifically, the melting temperature (T m ) increased when the samples were aged at 140 °C. Meanwhile, the DC breakdown strength of unfilled polypropylene reduced significantly after aging at 140 °C when compared to polypropylene nanocomposites.
科研通智能强力驱动
Strongly Powered by AbleSci AI