Poly(azobenzene acrylate-co-fluorinated acrylate) Spin-Coated Films: Influence of the Composition on the Photo-Controlled Wettability

The wetting properties of spin-coated films of copolymers based on azobenzene and fluorinated units have been investigated. The copolymers, denoted as poly(Azo-co-AcRf6), have been synthesized by free-radical polymerization of different proportions of acrylate monomers bearing either an azobenzene group or a semifluorinated side chain. The UV-visible spectroscopy analysis of the different spin-coating films through a cycle of UV and visible light irradiation indicates the reversible trans-cis isomerization of azobenzene groups. Simultaneously, atomic force microscopy shows that surface roughness does not exceed 1 nm. Advancing and receding contact angles of water and diiodomethane have been measured before and after UV photoirradiation of the different surfaces. In particular, a decrease in the advancing contact angles has been observed upon trans-cis isomerization of azobenzene groups. Switching variations up to 50° have been evidenced without any introduction of surface nanoroughness. Surface free-energy evaluations have been deduced from these measurements, including dispersive and polar components. The results show that, through surface composition and UV photoirradiation, a large range of surface free-energies can be obtained, from 7 to 46 mN·m(-1).