The Effect of Interpass Temperature on the Mechanical Properties and Microstructure of Components Made by the WAAM Method from Inconel 718 Alloy

The following study examines the impact of temperature on the deposition of components using Cold Metal Transfer–Wire Arc Additive Manufacturing technology. In the experiment, two overlay weld wall structures were created by applying an interpass temperature of 100 °C and without additional cooling. Subsequently, the microstructural and mechanical properties were observed. No changes in the microstructure due to the application of the interpass temperature were confirmed, and the microstructure of the manufactured components, in both cases, consisted of columnar dendrites. It was found that applying an interpass temperature reduced the average ultimate tensile strength by nearly 65 MPa and the average offset yield strength by 82 MPa. The influence of the cooling strategy on the resulting microstructure was not confirmed. Transmission electron microscopy analysis confirmed the presence of strengthening phases γ′/γ″ in both components; however, a larger amount of the strengthening phase γ″ was found in the component manufactured without the application of an interpass temperature.