Characteristics of a thick film ethanol gas sensor made of mechanically treated LaFeO3 powder

In this work, fabrication of LaFeO3 thick film ceramics for ethanol gas sensor made of mechanically treated (milling) powder was studied. The thick films were fabricated using screen printing technique from LaFeO3 powder treated by HEM (High Energy Milling). The films were baked at 800°C for one hour and analyzed using XRD and SEM. Sensitivity of the films was studied by measuring resistance of them at various temperatures in a chamber containing air with and without ethanol gas. Data of XRD showed that the thick film crystalizes in orthorombic structure with space group of Pn*a. SEM data showed that the films consisted of small grains with grain size of about 225 nm. According to the electrical data, the LaFeO3 thick films that produced in this work could be applied as ethanol gas with operating temperature of about 275°C.