Mou Honglin,Zhipeng Cai,Guozheng Ma,Licheng Zhou,Zhu Xianyong,Liu Ming,Haidou Wang,Xie Feng-kuan,Xin-Yang Wang
标识
DOI:10.1016/j.ceramint.2023.07.135
摘要
Hexagonal boron nitride (hBN) with excellent self-lubrication performance is expected to relieve the friction resistance and wear of NiCr–Cr3C2 coatings. However, the poor wettability of hBN with most materials makes it difficult to fabricate NiCr–Cr3C2-hBN composite coating with good cohesion strength. In this study, hBN was firstly pretreated through magnetron-sputtering aided Ni plating to form [email protected] particles. Then, NiCr–Cr3C2[email protected] powder was prepared by spray granulation. Next, corresponding coatings were prepared through supersonic atmosphere plasma spraying. It was found that in comparison with NiCr–Cr3C2-hBN coating, the NiCr–Cr3C2[email protected] coating exhibited a decreased porosity (from 3.6% to 0.3%), elevated cohesion (from 52.78 N to 62.11 N), and the wear rate decreased by an order of magnitude. It was concluded that [email protected] can effectively improve the component interface inside powder, enhance the cohesion of molten in-flight particles, and make the internal structure of the coating denser.
科研通智能强力驱动
Strongly Powered by AbleSci AI