Functional cellulose-derived epoxy cross-linked with BADGE resin to construct high-performance epoxy composites

The development of equipped bio-based epoxy materials has been gaining much attention recently. Nevertheless, finding the balance between the structure and properties of materials remains a significant challenge. In this work, cellulose-based epoxy (PHPCEP) with "soft" and "hard" cooperative structures was designed and demonstrated to endow bisphenol A diglycidyl ether (BADGE) with excellent toughness, heat resistance, mechanical strength, glass transition temperature, thermal stability, and solvent resistance. When 5 wt% PHPCEP was incorporated into BADGE composites, the resulting materials exhibited the maximum flexural strength (121.9 MPa) and tensile strength (71.4 MPa), a high glass transition temperature (148.3 °C), and 10 wt% PHPCEP/BADGE demonstrated the highest impact strength (70.5 kJ/m2). These figures are 18.8 %, 16.1 %, 21.5 %, and 254.3 % higher than the corresponding values of neat BADGE. The results of dynamic mechanical properties and heat degradation of the cured specimens also suggest that PHPCEP/BADGE materials have superior stiffness and toughness than neat BADGE, which could be attributed to the strong interaction between PHPCEP and BADGE, delivering better thermal stability for the composites compared to the pristine resin. Considering the remarkable effect, this work provides an effective way of highly efficient utilization of abundant cellulose and a high-performance additive for composite materials.