Enhancing Thermoelectric and Cooling Performance of Bi0.5Sb1.5Te3 through Ferroelectric Polarization in Flexible Ag/PZT/PVDF/Bi0.5Sb1.5Te3 Film

Bi₂Te₃-based thin films are gaining recognition for their remarkable room temperature thermoelectric performance. Beyond the conventional "process-composition-performance" paradigm, it is highly desirable to explore new methods to enhance their performance further. Here, we designed a sandwich-structured Ag/PZT/PVDF/Bi_0.5Sb_1.5Te₃(BST) thin film device and effectively regulated the performance of the BST film by controlling the polarization state of the PZT/PVDF layers. Results indicate that polarization induces interlayer charge redistribution and charge transfer between PZT/PVDF and BST, thereby achieving the continuous modulation of the electrical transport characteristics of BST films. Finally, following polarization at a saturation voltage of 3 kV, the power factor of the BST film increased by 13% compared to the unpolarized condition, reaching 20.8 μW cm^-1 K^-2. Furthermore, a device with 7 pairs of P-N legs was fabricated, achieving a cooling temperature difference of 11.0 K and a net cooling temperature difference of 2.4 K at a current of 10 mA after the saturation polarization of the PZT/PVDF layer. This work reveals the critical effect of introducing ferroelectric layer polarization to achieve excellent thermoelectric performance of the BST film.