Chen Liu,Shitong Wei,Shanping Lu
标识
DOI:10.1016/j.corsci.2023.111042
摘要
The corrosion behaviors of 9Cr-Si heat resistant steel deposited metals with different Si contents in oxygen-saturated static lead-bismuth eutectic at 550 °C were investigated. The results indicates that the oxide scale has a three-layer structure, including outer layer, inner layer, and inner oxidation zone (IOZ). The growing rate of oxide scale decreases with the increasing Si content in steel. The oxidation mechanism of high Si 9Cr deposited metal was discussed. IOZ presents emergence, disappearance, and regeneration in the corrosion process, while the inner layer divides into two sublayers during oxidation.